The characteristics and potency of limestone-based carbonate hydroxyapatite to viability and proliferation of human umbilical cord mesenchymal stem cell Rianti Devi1, Kristanto Wahyudi2, Damayanti Herlina2, Putri Tansza S.1, Dinaryanti Aristika3, Syahrom Ardiyansyah4,*, Yuliati Anita1,** 1Department of Dental Material, Faculty of Dental Medicine, Airlangga University, Jl. Mayjen. Prof. Dr. Moestopo No. 47, Surabaya, 60132, Indonesia 2Balai Besar Keramik Indonesia, Jl Jend. Ahmad Yani No 392, Bandung, 40272, Indonesia 3Stem Cell Research and Development Center, Institute of Tropical Disease - Airlangga University Gd. Lembaga Penyakit Tropis Lt. 1, Kampus C Universitas Airlangga Jln. Mulyorejo, Surabaya, 60115, Indonesia 4Medical Devices and Technology Centre (MEDITEC), Institute of Human Centered and Engineering (iHumEn), Universiti Teknologi Malaysia, 81310, UTM, Skudai, Johor, Malaysia *ardiyans@gmail.com
**Corresponding Author E-mail: anita-y@fkg.unair.ac.id
Online published on 20 February, 2023. Abstract Background Limestone primarily consists of CaCO3 (calcium carbonate), which have a similarity to one of human bone component, hydroxyapatite (HA), an element of apatite group (Ca10(PO4)6(OH)2). There were several setbacks in the use of artificial hydroxyapatite in the bone repair process; one of them was its relatively higher crystallinity level compared to those of human bone apatite. The addition of carbonate element to hydroxyapatite could improve its characteristics, such as increasing the solubility, decreasing the crystallinity, and changing the morphology of the crystal. That caused carbonate hydroxyapatite is preferable to help in the bone repair process. Aims This study aimed to find the effect of limestone-based CHA on viability and proliferation of hUMSCs, thus discovering the potential of CHA as a bone graft biomaterial candidate derived from limestone. Methods This study used FTIR, EDX, and XRD assays to CHA powder sample derived from limestone found in Padalarang and Cirebon extracted by BBK. Two grams of the sample were placed in the sample holder and examined by computer software. EDX assay was conducted three times in three different points, and the means were recorded. In the XRD assay, a carbon tip was put to the sample holder to allow sample attachment. The recorded data was compared to JCPDS data. Toxicity and proliferation examination of CHA were conducted through MTT assay in human umbilical cord mesenchymal stem cell (hUCMSC) cell lines with four different doses: 50μg/ml, 25μg/ml, 12,5μg/ml, and 6,25μg/ml. Results Limestone-based CA has hydroxyl (OH-), phosphate (PO42-), and carbonate (CO32-) functional groups. It has crystal particle formation and consists of O, Ca, and P elements. The result of the MTT assay showed limestone-based CHA is not toxic in all concentrations and has the proliferative ability. There were significant differences between the control and treatment groups. Conclusion CHA has OH-, PO42-, and CO32- function group. It has crystal particle formation and O, Ca, and P elements as its composition, with a Ca/P ratio of 1,67. It shows no toxicity to hUCMSC in all doses and has the ability to stimulate hUCMSC proliferation. Top Keywords Carbonate Hydroxyapatite, Limestone, Medicine, Cytotoxicity, Mesenchymal Stem Cells. Top |